ZrO2, Al2O3, ZrO2/Al2O3 and Al2O3/ZrO2 coatings were fabricated on low carbon steel using atmospheric plasma spraying technique. The microstructure and phase composition of the as-sprayed coatings were examined by scanning electron microscopy (SEM) and X-ray diffraction (XRD), respectively. The polarization test, salt spray test and immersion test were used to investigate the corrosion behavior of the coatings in 3.5% NaCl solution. The results suggested that the bilayered Al2O3/ZrO2 coating exhibits superior corrosion resistance when compared with the other coatings. This is ascribed to the presence of very few interconnected pores and stable phases in the coating. © 2016 The Nonferrous Metals Society of China

Sathish A-S

VIT Business School

Chennai Campus

Geetha M

Department of Control and Automation

School of Electrical Engineering

Vellore Campus

Vellore Institute of Technology (VIT) is a private university located in&nbsp;Tamil Nadu, India. Founded in 1984, as Vellore Engineering College, the institution offers 20 undergraduate, 34 postgraduate, four integrated and four research programs. It has campuses in Vellore, Amravati, Bhopal and Chennai.

VIT is one of the top ranked private universities in India according to NIRF, THE and QS Rankings.&nbsp;Govt. of India has recognized&nbsp;VIT, Vellore as an&nbsp;Institution of Eminence. This has allowed VIT to take independent quality initiatives and move up in world ranking.

&nbsp;

&nbsp;

VIT University

Comparative study on corrosion behavior of plasma sprayed Al2O3, ZrO2, Al2O3/ZrO2 and ZrO2/Al2O3 coatings

Transactions of Nonferrous Metals Society of China

This paper reports on the sliding wear performance of the nanostructured Al2O3-13TiO2, ZrO2 and the bilayered (ZrO2/Al2O3-13TiO2) coated biomedical Ti-13Nb-13Zr alloy in simulated body fluid condition. The nanopowders were sprayed using an atmospheric plasma spray technique and the reciprocatory sliding wear behavior of all the above coatings was evaluated using wear testing machine. The bilayered (ZrO2/Al2O3-13TiO2) coating which has not been reported hitherto exhibited two hundred and five hundred fold increase in the wear resistances when compared with that of the nanostructured Al2O3-13TiO2 (AT) and ZrO2 (YSZ) coatings. This substantial improvement in the wear resistance of the bilayered coating is attributed to its lower porosity and higher adhesion strength when compared to the AT and YSZ coatings. This study suggests that this new type of bilayered coating may be a preferred approach to be tried for obtaining much higher wear resistant coatings. © 2011 Elsevier B.V.

Wear

Sliding wear behavior of plasma sprayed nanoceramic coatings for biomedical applications

Biomedical Ti alloys are prone to undergo degradation due to the combined effect of wear and corrosion. To overcome these problems, surface modification techniques are being used. In this paper, the biomedical Ti alloy Ti-13Nb-13Zr was plasma sprayed with nanostructured Al2O3-13 wt%TiO2, yttria stabilized zirconia powders and bilayer containing alternate layers of the two coatings to improve the corrosion resistance and microhardness of the substrate. The plasma sprayed coatings were characterized by X-ray diffraction, scanning electron microscopy and Raman spectroscopy. The microstructure, microhardness and surface roughness of the coatings were investigated. The corrosion resistance of the coatings was studied in simulated body conditions. The results show improved corrosion resistance for the bilayered coating compared to the individual plasma sprayed coatings on biomedical Ti-13Nb-13Zr alloy substrate. © 2011 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Ceramics International

Studies on plasma sprayed bi-layered ceramic coating on bio-medical Ti–13Nb–13Zr alloy

Vacuum

Diary

Materials & Design

A study on sliding and erosive wear behaviour of atmospheric plasma sprayed conventional and nanostructured alumina coatings

Wear behavior of plasma sprayed composite coatings with in situ formed Al2O3

Journal	Data powered by TypesetTransactions of Nonferrous Metals Society of China
Publisher	Data powered by TypesetElsevier BV
ISSN	1003-6326
Open Access	0