Synthetic calcium hydroxyapatite (HAP, Ca10 (PO 4)6 (OH)2) is a well-known bioceramic material used in orthopedic and dental applications because of its excellent biocompatibility and bone-bonding ability due to its structural and compositional similarity to human bone. Here we report, for the first time, the synthesis of HAP by combustion employing tartaric acid as a fuel. Calcium nitrate is used as the source of calcium and diammonium hydrogen phosphate serves as the source of phosphate ions. Reaction processing parameters such as the pH, fuel-oxidant ratio and autoignition temperature are controlled and monitored. The products were characterized by powder x-ray diffraction, which revealed the formation of a hexagonal hydroxyapatite phase. Fourier transform infrared spectroscopy (FT-IR) spectra showed that the substitution of a carbonate ion occurs at the phosphate site. The morphology of the particles was imaged by scanning electron microscopy, which also revealed that the particles are of submicron size. Thermal analysis showed that the phase formation takes place at the time of combustion. Surface area and porosity analysis showed that the surface area is high and that the pores are of nanometer size. The mean grain size of the HAP powder, determined by the Debye-Scherrer formula, is in the range 20-30 nm. Chemical analyses to determine the Ca : P atomic ratio in synthesized ceramics were performed, and it was found to be 1 : 1.66. © 2008 National Institute for Materials Science.