Vellore Institute of Technology (VIT) is a private university located in&nbsp;Tamil Nadu, India. Founded in 1984, as Vellore Engineering College, the institution offers 20 undergraduate, 34 postgraduate, four integrated and four research programs. It has campuses in Vellore, Amravati, Bhopal and Chennai.

VIT is one of the top ranked private universities in India according to NIRF, THE and QS Rankings.&nbsp;Govt. of India has recognized&nbsp;VIT, Vellore as an&nbsp;Institution of Eminence. This has allowed VIT to take independent quality initiatives and move up in world ranking.

&nbsp;

&nbsp;

VIT University

Effect of Various Non Conventional Aging Treatments on the Mechanical Properties and Quality Indices of Cast and Heat Treated Components of Aluminum Alloy 354

GSTF Journal of Engineering Technology

Cast aluminium alloys are being employed increasingly in the automotive sector due to their light weight and excellent castability. This paper focuses on the strain hardening behaviour of Hipped and non-Hipped components of cast aluminium alloy 354 subjected to two-step ageing, as opposed to the routinely carried out single-step ageing. First step ageing (at 100°C) was carried out for 2 h and 5 h; ageing time at second step (at 170°C) was 1, 2 and 5 h. Mechanical properties and strain hardening behaviour were evaluated for different variants of two-step ageing treatment. Analysis of the results shows that the Hipped components have higher hardening capacity and generally higher strain hardening rate compared to the non-Hipped ones. Some of the two-step ageing treatments give mechanical properties comparable to the conventional T61 treatment, but with significantly higher strain hardening rate.

Advanced Materials Research

Strain Hardening Behaviour of Hipped and Non-Hipped Castings of Aluminium Alloy 354 Subjected to Two-Step Ageing Treatments

With the drive to build higher performance automobile engines, there has been a steady demand to further improve the mechanical behavior of the cast aluminum alloy 354 through improvements in processing. The present study explores the possibility of improving the tensile properties, quality indices Q &amp; QC and fatigue life of the alloy over those obtained by standard T61 treatment by adopting different modified aging treatments. These include i) lowering the artificial aging temperature ii) interrupted aging cycles similar to T6I4 referred to in the published literature and iii) artificial aging in two steps instead of in single step. Based on the results, a few modified aging treatments could be identified which lead to a comparable combination of tensile properties, but with improved fatigue life and a shade higher quality level. © 2014 The Minerals, Metals &amp; Materials Society.

Light Metals 2014

Effect of Modified Aging Treatments on the Tensile Properties, Quality Indices and Fatigue Life of Cast Components of Aluminum Alloy 354

Automotive industry makes wide scale use of cast aluminium alloy 354 in the production of crucial components, such as compressor wheels for turbochargers. The compressor wheels undergo T61 heat treatment, involving artificial ageing at 188°C. This study focuses on the possible improvement of the mechanical behaviour of the components by subjecting them to modified heat treatments involving usage of lower artificial ageing temperatures (160, 171 and 177°C). A comparative analysis of tensile properties and strain hardening behaviour has been carried out with different artificial ageing temperatures. Results showed that the heat treatment routinely employed by the industry (aged at 188°C) leads to overageing, thereby resulting in relatively inferior mechanical properties and lower strain hardening rates as compared to the samples heat treated at lower artificial ageing temperatures. It is concluded that lowering of the artificial ageing temperature can lead to a superior state of components with respect to mechanical behaviour.

Analysis of Strain Hardening Behaviour of Cast Aluminium Alloy 354 Subjected to Artificial Ageing at Various Temperatures

Effect of various non conventional aging treatments on the mechanical properties and quality indices of cast and heat treated components of aluminum alloy 354

Journal	GSTF Journal of Engineering Technology