The present study investigates the microstructure and mechanical properties of joints fabricated by Continuous and pulsed current gas tungsten arc welded alloy 600. Welding was done by autogenous mode. The macro examination was carried out to evaluate the welding defects in the weld joints. Optical and Scanning Electron Microscope (SEM) were performed to assess the microstructural changes in the fusion zone. Energy Dispersive Spectroscopy (EDS) analysis was carried to evaluate the microsegregation of alloying elements in the fusion zone. The tensile test was conducted to assess the strength of the weld joints. The results show that no welding defects were observed in the fusion zones of Continuous and Pulsed current Gas Tungsten Arc Welding. The refined microstructure was found in the pulsed current compared to continuous current mode. Microsegregation was not noticed in the weld grain boundary of continuous and pulsed current mode. The pulsed current shows improved mechanical properties compared to the continuous current mode. © Published under licence by IOP Publishing Ltd.

Manikandan M

Department of Design and Automation

School of Mechanical Engineering

Vellore Campus

Srikanth A

A Srikanth

Fulltext

Vellore Institute of Technology (VIT) is a private university located in&nbsp;Tamil Nadu, India. Founded in 1984, as Vellore Engineering College, the institution offers 20 undergraduate, 34 postgraduate, four integrated and four research programs. It has campuses in Vellore, Amravati, Bhopal and Chennai.

VIT is one of the top ranked private universities in India according to NIRF, THE and QS Rankings.&nbsp;Govt. of India has recognized&nbsp;VIT, Vellore as an&nbsp;Institution of Eminence. This has allowed VIT to take independent quality initiatives and move up in world ranking.

&nbsp;

&nbsp;

VIT University

Investigation on Microstructure and Mechanical Properties of Continuous and Pulsed Current Gas Tungsten Arc Welded alloy 600

IOP Conference Series: Materials Science and Engineering

Alloy 686 is a highly corrosion resistant 21st-Century Nickel based superalloy derived from Ni-Cr-Mo ternary system. The alloying elements chromium (Cr) and molybdenum (Mo) are added to improve the resistance to corrosion in the broad range of service environment. The presence of a higher percentage of alloying elements Cr and Mo lead to microsegregation and end up with hot cracking in the fusion zone of Nickel-based superalloys. However, there is scanty of information regarding the welding of alloy 686 with respect to the microsegregation of alloying elements. The present study investigates the possibility of bringing down the microsegregation to cut down the formation of secondary phases in the fusion zone. The weld joints were fabricated by Gas Tungsten Arc Welding (GTAW) and Pulsed current gas tungsten arc welding (PCGTAW) with ERNiCrMo-10 filler and without filler wire (autogenous) mode. The microstructural properties of the weld joints were studied with optical and Scanning Electron Microscope (SEM). The joints fabricated by pulsed current (PC) technique shows refined microstructure, narrower weld bead and practically no heat affected zone (HAZ). Scanning Electron Microscope demonstrates the presence of secondary phases in the interdendritic regions of GTAW case. Energy Dispersive X-ray Spectroscopy (EDS) analysis was carried out to evaluate the microsegregation of alloying element. The results show that the segregation of Mo noticed in the interdendritic zone of GTAW both autogenous and filler wire. Tensile and Impact tests were done to evaluate the strength, ductility, and toughness of the weld joints. The results show that the PCGTA helps to obtain improved strength, ductility and toughness of the weld joints compared to their respective GTAW. Bend test did not lead to cracking irrespective of the type of welding adopted in the present study. © 2017 Elsevier B.V.

Materials Science and Engineering: A

Development of welding technology for improving the metallurgical and mechanical properties of 21st century nickel based superalloy 686

Superalloy C-276 is known to be prone to hot cracking during fusion welding by Gas Tungsten Arc method. Microsegregation occurring during cooling of fusion zone with consequent appearance of topologically close-packed phases P and l has been held responsible for the observed hot cracking. The present work investigated the possibility of suppressing the microsegregation in weldments by resorting to current pulse. Weldments were made by continuous current gas tungsten arc welding and pulsed current gas tungsten arc welding using ERNiCrMo-4 filler wire. The weld joints were studied with respect to microstructure, microsegregation, and mechanical properties. Optical microscopy and scanning electron microscopy were employed to study the microstructure. Energy-Dispersive X-ray Spectroscopy was carried out to evaluate the extent of microsegregation. Tensile testing was carried out to determine the strength and ductility. The results show that the joints fabricated with pulsed current gave rise to narrower welds with practically no heat affected zone, a refined microstructure in the fusion zone, reduced microsegregation, and superior combination of mechanical properties. © The Chinese Society for Metals and Springer-Verlag Berlin Heidelberg 2014.

Acta Metallurgica Sinica (English Letters)

Improvement of Microstructure and Mechanical Behavior of Gas Tungsten Arc Weldments of Alloy C-276 by Current Pulsing

Effects of switching over from gas tungsten arc welding (GTAW) to pulsed current gas tungsten arc welding (PCGTAW) on the quality of joints produced in Hastelloy C-276 material were investigated. Welding was carried out both by autogenous mode and using ERNiCrMo-3 filler wire. Microstructures of weld joints produced with and without current pulsing were studied using optical and scanning electron microscopy. Microsegregation occurring in GTAW and PCGTAW joints was investigated using energy dispersive X-ray spectroscopy (EDS). Strength and ductility of weld joints produced with and without pulsing were evaluated. The results show that pulsing results in refined microstructure, reduced microsegregation and improved strength of weld joints. Secondary phase(s) noticed in GTA weldments were found to be absent in PCGTA weldments. Autogenous PCGTA weldments were found to be the best in terms of: (i) freedom from microsegregation, (ii) strength and (iii) freedom from unwanted secondary phases. © 2014 The Society of Manufacturing Engineers. Published by Elsevier Ltd. All rights reserved.