A finite element examination of the effect of delaminations on fracture characteristics of fibre metal laminate (Glare), by comparing energy release rates of normal cracks in laminates with and without delaminations, is presented in the paper. Glare comprising thin cracked 2024-T3 aerospace aluminum alloy layers alternately bonded with E-glass fibre based composite prepregs is considered for the analysis. Delaminations are modeled with interface cohesive elements. Energy release rates of normal cracks in laminates with delaminations are found to be higher than those in the laminates without delaminations.

Narayanan S

Department of Manufacturing Engineering

School of Mechanical Engineering

Vellore Campus

Bhat S

Vellore Institute of Technology (VIT) is a private university located in&nbsp;Tamil Nadu, India. Founded in 1984, as Vellore Engineering College, the institution offers 20 undergraduate, 34 postgraduate, four integrated and four research programs. It has campuses in Vellore, Amravati, Bhopal and Chennai.

VIT is one of the top ranked private universities in India according to NIRF, THE and QS Rankings.&nbsp;Govt. of India has recognized&nbsp;VIT, Vellore as an&nbsp;Institution of Eminence. This has allowed VIT to take independent quality initiatives and move up in world ranking.

&nbsp;

&nbsp;

VIT University

The paper presents a theoretical model for estimation of yield strength of fiber metal laminate. Principles of elasticity and formulation of residual stress are employed to determine the stress state in metal layer of the laminate that is found to be higher than the stress applied over the laminate resulting in reduced yield strength of the laminate in comparison with that of the metal layer. The model is tested over 4A-3/2 Glare laminate comprising three thin aerospace 2014-T6 aluminum alloy layers alternately bonded adhesively with two prepregs, each prepreg built up of three uni-directional glass fiber layers laid in longitudinal and transverse directions. Laminates with prepregs of E-Glass and S-Glass fibers are investigated separately under uni-axial tension. Yield strengths of both the Glare variants are found to be less than that of aluminum alloy with use of S-Glass fiber resulting in higher laminate yield strength than with the use of E-Glass fiber. Results from finite element analysis and tensile tests conducted over the laminates substantiate the theoretical model.

Fulltext

IOP Conference Series: Materials Science and Engineering

A Theoretical Model for Estimation of Yield Strength of Fiber Metal Laminate

International Journal of Fatigue

Modeling of fatigue crack growth in notched fiber metal laminates

Analytical prediction model for fatigue crack propagation and delamination growth in Glare

Numerical investigation of the effect of delaminations on fracture characteristics of glare

Publisher	AIP
Open Access	0