Accelerator based MeV ion implantation of Ca2+ and P2+ into the titanium substrate to form hydroxyapatite (HA) has been carried out. Calcium hydroxide was formed after heating the calcium implanted titanium in air at 80 °C for 3 h. Upon subsequent annealing for 5 min at 600 °C HA was formed on the surface. Penetration depth of the HA layer in this method is much higher as compared to keV ion implantation. By elemental analysis, Ca/P ratio of the HA was found to be 1.76 which is higher than the ideal 1.67. This higher Ca/P ratio is attributed to the higher penetration depth of the MeV technique used. © 2009 Elsevier B.V. All rights reserved.

Narayanan R

Mechanical

School of Mechanical Engineering

Chennai Campus

T.R. Rautray

T.-Y. Kwon

K.-H. Kim

Vellore Institute of Technology (VIT) is a private university located in&nbsp;Tamil Nadu, India. Founded in 1984, as Vellore Engineering College, the institution offers 20 undergraduate, 34 postgraduate, four integrated and four research programs. It has campuses in Vellore, Amravati, Bhopal and Chennai.

VIT is one of the top ranked private universities in India according to NIRF, THE and QS Rankings.&nbsp;Govt. of India has recognized&nbsp;VIT, Vellore as an&nbsp;Institution of Eminence. This has allowed VIT to take independent quality initiatives and move up in world ranking.

&nbsp;

&nbsp;

VIT University

Thin Solid Films

Accelerator based synthesis of hydroxyapatite by MeV ion implantation

Journal	Thin Solid Films
ISSN	00406090